HPb62-0.8 T35100 - GB /T 21652-2017

Grade	HPb62-0.8
China ISC	T35100
Corresponding Standard	GB /T 21652-2017 Copper and Copper Alloy Wire
Classification	Copper and Copper Alloys

HPb62-0.8 Chemical Element Composition Content (%)

Component	Fe	Cu	Pb	Other Total	More
Minimum Value	-	60	0.5	-	Zn:Residual
Maximum Value	0.2	63	1.2	0.75	Zn:Residual

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

• The iron content of anti-magnetic brass shall not exceed 0.03%.

HPb62-0.8 Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %
0.5~6.0	1/2硬(H02)	410~540	A_100mm ≥12
0.5~6.0	硬(H04)	450~560	/

Approximate Comparison Table Brass

China		United States	International Organization for Standardization	France	European Standard		Russia
GB	ISC	ASTM	ISO	NF EN/NF	EN	Numerical Grade	GOST
HPb62-0.8	T35100	62Cu-37.5Zn-0.5Pb	CuZn37Pb1	CuZn37Pb1	CuZn37Pb1	CW605N	ЛC62-0.8

HPb62-0.8 Corresponding Standards(Same grade name, different standards)

1	GB /T 5231-2012
	HPb62-0.8 T35100
2	GB /T 5231-2022
	HPb62-0.8 T35100
3	GB /T 5231-2001
	HPb62-0.8 62-0.8铅黄铜
4	GB /T 21652-2017
	HPb62-0.8 T35100
5	GB /T 21652-2008
	HPb62-0.8

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!