A681 Type D3 T30403 - ASTM A681-2024

Grade	A681 Type D3
USA UNS	T30403
AISI American Iron and Steel Institute	D3
Corresponding Standard	ASTM A681-2024 Tool Steels Alloy
Classification	Tool Steel

A681 Type D3 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	W	V	More
Minimum Value	2	0.1	0.1	-	-	11	-	-	Ni+Cu≤0.75
Maximum Value	2.35	0.6	0.6	0.03	0.03	13.5	1	1	Ni+Cu≤0.75

A681 Type D3 Mechanical Properties

condition	Heat Treatment or Condition	Hardness HBW
condition of delivery	Cold Drawing	BHN ≤269
condition of delivery	Annealing	BHN ≤255
specimen	Preheat to 816±14 ℃, heat to 968±5.6℃(controllable atmosphere) or 954℃(salt bath), hold for 10 to 20 min, oil cool. Temper at 204±5.6℃ once for 2 h	HRC ≥61

1 Approximate Comparison Table Alloy Tool Steel 1

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

Cr12

T21200

SKD 1

STD 1

T30403

X210Cr12

1.2080

X210Cr12
X200Cr12

Х12

X210Cr12
BD3

2 Approximate Comparison Table Alloy Tool Steel 2

A681TypeD3 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!