Q460D - GB /T 1591-1994

Grade	Q460D
Corresponding Standard	GB /T 1591-1994 High Strength Low Alloy Structural Steels
Classification	Alloy Steel

Q460D Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu ^*	Ti	V	Nb	Al
Minimum Value	-	-	1	-	-	-	-	-	0.02	0.02	0.015	0.015
Maximum Value	0.2	0.55	1.7	0.03	0.03	0.7	0.7	0.3	0.2	0.2	0.06	-

Q460D Mechanical Properties

thickness t mm	Test Temperature	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
t≤16	Room Temperature	550~720	≥460	≥17
16＜t≤35		550~720	≥440	≥17
35＜t≤50		550~720	≥420	≥17
50＜t≤100		550~720	≥400	≥17
specimen	-20°C				≥34

New and Old Grade Replacement List

1 Approximate Comparison Table Structural, Pressure Vessel and Engineering Steels

China	Japan	International Organization for Standardization	Germany	France	European Standard		Russia	United Kingdom
GB	JIS	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	GOST	BS EN/BS
Q460D	SM520B	E460	StE460	E460R	S460N FeE460KGN①	1.8901	18G2AF 18G2AFps	55C

2 Approximate Comparison Table High strength structural steel plates in the quenched and tempered condition

China	International Organization for Standardization	European Standard
GB	ISO	EN
Q460QD GB/T 16270-2009 Q460D GB/T 16270-1996	E460DD ISO 4950.3-2003	S460Q EN 10025-6-2004

3 Approximate Comparison Table High strength structural steel plates in the quenched and tempered condition

China	International Organization for Standardization
GB	ISO
Q460QD GB/T 34560.4-2017 Q460D GB/T 16270-2009	S460QD ISO 630-4-2012

Q460D Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!