X2CrNi 19 11 1.4306 - DIN 1654-5-1989

Grade	X2CrNi 19 11
Germany W-Nr.	1.4306
Corresponding Standard	DIN 1654-5-1989 Cold heading and Cold Extruding Steels Technical Delivery Conditions for Stainless Steels
Classification	Austenitic Stainless Steel

X2CrNi 19 11 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni
Minimum Value	-	-	-	-	-	18	10
Maximum Value	0.03	1	2	0.045	0.03	20	12.5

X2CrNi 19 11 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Impact Energy Absorption KV2 J
Steel	quenching or quenching + peeling	≤630			≥55
Steel	Cold draw + quenching	≤630			≥55
Steel	Cold draw + quenching + slightly cold redraw (K+GKZ+K)	≤680			≥55
Steel	quenching	460~680	≥180	≥50		≥60

New and Old Grade Replacement List

Corresponding Standard	Grade
DIN 1654-5-1989	Grade Germany W-Nr.
DIN EN 10263-5-2002	Grade Germany W-Nr.
DIN EN 10263-5-2018	Grade Germany W-Nr.

1 Approximate Comparison Table Austenitic Stainless Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

Russia

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

Numerical Grade

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

BS EN/BS

022Cr19Ni10
(00Cr19Ni10)

S30403

304L

SUS 304L

STS 304L

304L

S30403

X2CrNi 19-11
X2CrNi 18-9

4306-304-03-I
4307-304-03-I

X2CrNi 19-11
(X2CrNi 18-9)

1.4306

Z2CN 18-10
Z2CN 18-09

X2CrNi 19-11
X2CrNi 18-9

1.4306
1.4307

03Х18Н10

304S12

2 Approximate Comparison Table Corrosion-Resistant Cast Steels

China	Japan	United States	Germany		France	Russia	United Kingdom
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG00Cr18Ni10	SUS19	CF3	G-X2CrNi18 9	1.4306	Z2CN18.10M	Х18Н8Л(旧号)	304C12

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!