X2CrNiN 18 10 1.4311 - DIN 1654-5-1989

Grade	X2CrNiN 18 10
Germany W-Nr.	1.4311
Corresponding Standard	DIN 1654-5-1989 Cold heading and Cold Extruding Steels Technical Delivery Conditions for Stainless Steels
Classification	Austenitic Stainless Steel

X2CrNiN 18 10 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	N
Minimum Value	-	-	-	-	-	17	8.5	0.12
Maximum Value	0.03	1	2	0.045	0.03	19	11.5	0.22

X2CrNiN 18 10 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Impact Energy Absorption KV2 J
Steel	quenching or quenching + peeling	≤730			≥55
Steel	Cold draw + quenching	≤730			≥55
Steel	Cold draw + quenching + slightly cold redraw (K+GKZ+K)	≤790			≥55
Steel	quenching	550~760	≥270	≥40		≥60

Approximate Comparison Table Austenitic Stainless Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

BS EN/BS

022Cr19Ni10N
(00Cr18Ni10N)

S30453

304LN

SUS 304LN

STS 304LN

304LN

S30453

X2CrNiN 18-9
X2CrNiN18-10

X2CrNiN 18-10

1.4311

Z2CN 18-1Az
Z3CN18-10Az

X2CrNiN 18-10

1.4311

2371

304S62
304S61

X2CrNiN1810 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!