C2C 1.0314 - DIN EN 10263-2-2002

Grade	C2C
Germany W-Nr.	1.0314
Corresponding Standard	DIN EN 10263-2-2002 Steel Rod,bars and Wire for Cold Heading and Cold Extrusion - Part 2: Technical Delivery Conditions for Steels Not Intended for Heat Treatment after Cold Working
Classification	Carbon Steel

C2C Chemical Element Composition Content (%)

Component	C	Si	Mn ^①	P	S	Al ^②
Minimum Value	-	-	0.2	-	-	0.02
Maximum Value	0.03	0.1	0.4	0.02	0.025	0.06

C2C Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
5＜d≤100	+U 或+U+PE	≤360	≥75
5＜d≤10	+U+C	≤450	≥70
10＜d≤40	+U+C	≤440	≥70
40＜d≤100	+U+C	≤440	≥68
2＜d≤5	+U+C+AC	≤310	≥80
5＜d≤100	+U+C+AC	≤300	≥80
2＜d≤5	+U+C+AC+LC	≤350	≥75
5＜d≤100	+U+C+AC+LC	≤340	≥75

Approximate Comparison Table High-Quality Carbon Structural Steel

C2C Corresponding Standards(Same grade name, different standards)