2017 - GB /T 3195-2023

Grade	2017
Corresponding Standard	GB /T 3195-2023 Aluminium and Aluminium Alloys Drawn (Rolled) Round Wire
Classification	Aluminum and Aluminum Alloys

2017 Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Cu	Ti	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	0.2	0.4	-	3.5	-	-	0.4	-	-	Al:Rem
Maximum Value	0.7	0.8	1	0.1	4.5	0.15	0.25	0.8	0.05	0.15	Al:Rem

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

2017 Mechanical Properties

diameter d mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
1.6~10	2017-H13	Work Hardening - 3/8 Hard (H13)	205~275
1.6~10	2017-T42	Solution Heat Treatment + Natural Aging (T42)	≥380	≥220	-	- ≥10

Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China	Japan	United States		International Organization for Standardization		Germany		European Standard
GB	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN
2017	2017 A92017	2017	A92017	AlCu4MgSi	A92017	AlCu4Mg1	3.1325 A92017	EN-AW-AlCu4MgSi

2017 Corresponding Standards(Same grade name, different standards)

1	JIS H 4040-2006
	2017 A2017 W A2017 BD A2017 BE
2	GB /T 3195-2016
	2017
3	GB /T 3190-2020
	2017
4	JIS H 4040-2015
	2017 A2017 W A2017 BD A2017 BE
5	ISO 209-2007
	2017 (AlCu4MgSi)
6	GB /T 3191-2019
	2017
7	GB /T 3880.1-2012
	2017
8	GB /T 3195-2023
	2017

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!