C35E 1.1181 - EN 10269-2013

Grade	C35E
European Standard Steel Grade	1.1181
Corresponding Standard	EN 10269-2013 Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
Classification	Carbon Steel
Density	7.85 g/cm³

C35E Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S ^*	Cr	Ni	Mo	More
Minimum Value	0.32	-	0.5	-	-	-	-	-	Cr+Mo+Ni： ≤0.63
Maximum Value	0.39	0.4	0.8	0.03	0.015	0.4	0.4	0.1	Cr+Mo+Ni： ≤0.63

C35E Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Impact Energy Absorption KV2 J
d≤60	+N	500~650	≥300	≥20	-	≥27
d≤60	+QT	500~650	≥300	≥22	≥45	≥55
60<d≤150	+QT	500~650	≥300	≥22	≥45	≥39

1 Approximate Comparison Table

China	Japan	International Organization for Standardization	European Standard
GB	JIS	ISO	EN	Numerical Grade
35	S35C	C35E	C35E	1.1181

2 Approximate Comparison Table

China	Japan	United States	International Organization for Standardization	Germany	France	European Standard		Russia	Sweden	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
35	S35C	1035	C35E4	Ck35	XC38 XC38H1	C35E	1.1181	35	1572	080M36 CFS6

3 Approximate Comparison Table

China	United States	International Organization for Standardization	European Standard
GB	ASTM/AISI	ISO	EN	Numerical Grade
35Mn (GB/T 699-2015)	1037 (ASTM A29/A29M:2005)	C35E4 (ISO 683-18:1996)	C35E (EN 10083-1:1991+A1:1996) (EN 10084:1998)	1.1181

C35E Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!