ZG 200-400 ZG15 - GB /T 11352-2009

Grade	ZG 200-400
Old Grade
Corresponding Standard	GB /T 11352-2009 Carbon steel castings for general engineering purpose
Classification	Carbon Steel

ZG 200-400 Chemical Element Composition Content (%)

Component	C ^①	Si	Mn ^①	P	S	Cr ^②	Ni ^②	Cu ^②	Mo ^②	V ^②
Minimum Value	-	-	-	-	-	-	-	-	-	-
Maximum Value	0.2	0.6	0.8	0.035	0.035	0.35	0.4	0.4	0.2	0.05

ZG 200-400 Mechanical Properties

Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Impact Energy Absorption KV2 J
≥400	≥200	≥25	* ≥40	KV：≥30* KU：≥47*

1 Approximate Comparison Table Cast Steel

2 Approximate Comparison Table Cast Steel

China	Japan	United States	International Organization for Standardization	Germany		France	Russia	United Kingdom
GB	JIS	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG200-400	SC360	J01700	200-400	GS-38 GS-CK16	1.0416 1.1142	E20-40M	15Л	AW,CLA9

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!