3Cr2W8V T23273 T20280 - GB /T 1299-2014

3Cr2W8V Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	W	V
Minimum Value	0.3	-	-	-	-	2.2	7.5	0.2
Maximum Value	0.4	0.4	0.4	0.03	0.03	2.7	9	0.5

3Cr2W8V Mechanical Properties

condition	Heat Treatment or Condition	Hardness HBW
Delivery condition	Annealing	≤255
sample	Quenching	HRC*

1 Approximate Comparison Table Hot Work Tool Steel

China		Japan	United States	International Organization for Standardization
GB	ISC	JIS	ASTM	ISO
3Cr2W8V	T23273	SKD 5	H21	X30WCrV 9-3

2 Approximate Comparison Table Hot-Work Tool Steels

China	Japan	United States	International Organization for Standardization	Germany	France	European Standard		Russia	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	GOST	BS EN/BS
3Cr2W8V	SKD5	H21	X30WCrV9-3	X30WCrV9-3	Z30WCV9	X30WCrV9-3	1.2581	3KH2V8F	BH21

3Cr2W8V Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!