Grade	PH13-8Mo
Corresponding Standard	SAE AMS 5629G-2015 Steel, Corrosion-Resistant, Bars, Wire, Forgings, Rings, and Extrusions 13Cr - 8.0Ni - 2.2Mo - 1.1Al Vacuum Induction Plus Consumable Electrode Melted Solution Heat Treated, Precipitation Hardenable （Composition similar to UNS S13800）
Classification	Precipitation-Hardening Stainless Steel
Properties	High Strength Corrosion Resistance Impact Resistance

PH13-8Mo Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo	N	Al
Minimum Value	-	-	-	-	-	12.25	7.5	2	-	0.9
Maximum Value	0.05	0.1	0.1	0.01	0.008	13.25	8.5	2.5	0.01	1.35

PH13-8Mo Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Longitudinal	H950	≥1517	≥1413	≥10	≥45	≤363
Transverse	H950	≥1517	≥1413	≥10	≥35	≤363
Longitudinal	H1000	≥1413	≥1310	≥10	≥50	≤363
Transverse	H1000	≥1413	≥1310	≥10	≥40	≤363
Longitudinal	H1025	≥1276	≥1207	≥11	≥50	≤363
Transverse	H1025	≥1276	≥1207	≥11	≥40	≤363
Longitudinal	H1050	≥1207	≥1138	≥12	≥50	≤363
Transverse	H1050	≥1207	≥1138	≥12	≥40	≤363
Longitudinal	H1100	≥1034	≥931	≥14	≥50	≤363
Transverse	H1100	≥1034	≥931	≥14	≥50	≤363
Longitudinal	H1150	≥931	≥621	≥14	≥50	≤363
Transverse	H1150	≥931	≥621	≥14	≥50	≤363

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!