S11100 - ASTM A564/A564M-2019 - H2ABC

中文版

USA UNS	S11100
Corresponding Standard	ASTM A564/A564M-2019(a) Standard Specification for Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes
Classification	Precipitation-Hardening Stainless Steel
Properties	Corrosion Resistance

Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo	N	Ti	Al
Minimum Value	-	-	-	-	-	11	10.25	1.75	-	0.2	1.35
Maximum Value	0.02	0.25	0.25	0.015	0.01	12.5	11.25	2.25	0.01	0.5	1.75

Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Steel	Solution treatment (A): 840±14°C, oil or water quenching, hold at -73°C for at least 8h, air cooling					HRC: ≤36 HB: ≤331
Steel; t≤300 (longitudinal)	Quenching and/or Aging (H900): 480°C hold for 4h~8h air or oil or water cooling	≥1700	≥1590	≥11	≥43	HRC: ≥47 HB: ≥448
Steel; t≤300 (longitudinal)	Quenching and/or aging (H950): 510°C, hold for 8h, air, oil, or water cooling	≥1655	≥1517	≥10	≥45	HRC: ≥47 HB: ≥448
Steel; t≤300 (transverse)	Quenching and/or aging (H950): 510°C, hold for 8h, air, oil, or water cooling	≥1655	≥1517	≥8	≥35	HRC: ≥47 HB: ≥448
Steel; t≤300 (longitudinal)	Quenching and/or aging (H1000): 540°C, hold for 8h, air, oil or water cooling	≥1517	≥1378	≥10	≥50	HRC: ≥45 HB: ≥426
Steel; t≤300 (transverse)	Quenching and/or aging (H1000): 540°C, hold for 8h, air, oil or water cooling	≥1517	≥1378	≥10	≥40	HRC: ≥45 HB: ≥426

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!