QT400-18 QT400-18L QT400-18A - YB /T 036.2-1992 - H2ABC

中文版

Grade	QT400-18
Other Names
Corresponding Standard	YB /T 036.2-1992
Classification	cast Iron

QT400-18 Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
QT400-18 (separately cast samples)	≥400	≥250	≥18	130~180	room temperature 23±5℃ ≥11
QT400-18L(separately cast samples)					low temperature -20±2℃ ≥10
QT400-18A(cast-in samples) wall＞30~60mm	≥390	≥250	≥18	130~180	room temperature 23±5℃ ≥11
QT400-18A (cast-in samples) wall＞60~200mm	≥370	≥240	≥12	130~180	≥10
QT400-18AL (cast-in samples) wall ＞30~60mm					low temperature -20±2℃ ≥10
QT400-18AL (cast-in samples) wall＞60~200mm					≥8

Approximate Comparison Table cast iron

China	Japan	United States	International Organization for Standardization	France	European Standard		Sweden	United Kingdom	Australia
GB	JIS	ASTM	ISO	NF EN/NF	EN	Numerical Grade	SS	BS EN/BS	Australian Standard AS
QT400-18	FCD400-18	60-40-18	400-18 400-18/S 400-18/U	400-18 FGS400-18	EN-GJS-400-18	5.3105 (EN-JS1020)	0717-02	400/18	300-17

QT400-18 Corresponding Standards(Same grade name, different standards)

1	GB /T 1348-2019
	QT400-18
2	YB /T 036.2-1992
	QT400-18 QT400-18L QT400-18A QT400-18AL
3	GB /T 1348-2009
	QT400-18

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!