HT350 - YB /T 036.2-1992

Grade	HT350
Corresponding Standard	YB /T 036.2-1992 General Technical Conditions for Metallurgical Equipment Manufacturing - Cast Iron Parts
Classification	cast Iron

HT350 Mechanical Properties

	Tensile Strength σ_b Mpa
Single Cast Test Bar	≥350
Casting Wall Thickness > 10~20mm	≥340
Casting Wall Thickness > 20~30mm	≥290
Casting Wall Thickness > 30~50mm	≥260
Attached Cast Test Bar, Wall Thickness > 20~40mm (φ30mm)	≥300
Attached Cast Test Bar, Wall Thickness > 40~80mm (φ30mm)	≥270
Attached Cast Test Bar, Wall Thickness > 40~80mm (φ50mm)	≥265
Attached Cast Test Bar, Wall Thickness > 80~150mm (φ50mm)	≥240
Attached Cast Test Bar, Wall Thickness > 150~300mm (φ50mm)	≥215
Attached Cast Test Block, Wall Thickness > 20~40mm (R15mm)	≥290
Attached Cast Test Block, Wall Thickness > 40~80mm (R15mm)	≥260
Attached Cast Test Block, Wall Thickness > 80~150mm (R25mm)	≥230
Attached Cast Test Block, Wall Thickness > 150~301mm (R25mm)	≥210

Approximate Comparison Table Cast Iron

China

Japan

United States

International Organization for Standardization

Germany

France

European Standard

Russia

Sweden

United Kingdom

Australia

JIS

ASTM

SAE

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

BS EN/BS

Australian Standard AS

HT350

FC350

50
350

G13H24

350
JL350

GG35

0.6035

FGL350

EN-GJL-350

EN-JL1060

SCH35

0135

350

T350

HT350 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!