SUS F 410-A SUS F 410-B SUS F 410-C - JIS G 3214-1991 - H2ABC

中文版

Grade	SUS F 410-A
Other Names
Corresponding Standard	JIS G 3214-1991 Stainless steel forgings for pressure vessels
Classification	Martensitic Stainless Steel
Properties	Corrosion Resistance

SUS F 410-A Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni
Minimum Value	-	-	-	-	-	11.5	-
Maximum Value	0.15	1	1	0.04	0.03	13.5	0.5

SUS F 410-A Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
SUS F 410-A	Quenching + Tempering	≥480	≥275	≥16	≥35	143~187
SUS F 410-B	Quenching + Tempering	≥590	≥380	≥16	≥35	167~229
SUS F 410-C	Quenching + Tempering	≥760	≥585	≥14	≥35	217~302
SUS F 410-D	Quenching + Tempering	≥900	≥760	≥11	≥35	262~321

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!