A681 Type D2 T30402 - ASTM A681-2008(R2015)

Grade	A681 Type D2
USA UNS	T30402
AISI American Iron and Steel Institute	D2
Corresponding Standard	ASTM A681-2008(R2015) Standard Specification for Tool Steels Alloy
Classification	Tool Steel

A681 Type D2 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Mo	V	More
Minimum Value	1.4	0.1	0.1	-	-	11	0.7	0.5	Ni+Cu≤0.75
Maximum Value	1.6	0.6	0.6	0.03	0.03	13	1.2	1.1	Ni+Cu≤0.75

A681 Type D2 Mechanical Properties

form	Heat Treatment or Condition	Hardness HBW
Bars, Thick Plates, Thin Plates, Strips, Rods, Wires, Forgings	Cold Drawing	BHN ≤269
Bars, Thick Plates, Thin Plates, Strips, Rods, Wires, Forgings	Annealing	BHN ≤255
Bars, Thick Plates, Thin Plates, Strips, Rods, Wires, Forgings	Heat Treatment	HRC ≥59

1 Approximate Comparison Table Alloy Cold-Work Tool Steel

China	Japan	United States	International Organization for Standardization
GB	JIS	ASTM	ISO
Cr12Mo1V1	SKD 10	D2	X153CrMoV12

2 Approximate Comparison Table Alloy Tool Steel 1

China		Japan	United States		International Organization for Standardization	Germany		France	United Kingdom
GB	ISC	JIS	ASTM	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
Cr12Mo1V1	T21202	SKD 10	D2	T30402	X153CrMoV12	X155CrVMo12-1	1.2379	X153CrMoV12	X153CrMoV12 BD2

3 Approximate Comparison Table Alloy Tool Steel 2

A681TypeD2 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!