Grade F593 410
USA UNS S41000
Corresponding Standard ASTM F593-2017
Standard Specification for Stainless Steel Bolts, Hex Cap Screws, and Studs
Classification Martensitic Stainless Steel
F593 410 Chemical Element Composition Content (%)
Component C Si Mn P S Cr
Minimum Value - - - - - 11.5
Maximum Value 0.12 1 1 0.04 0.03 13.5
F593 410 Mechanical Properties
Heat Treatment or Condition
Tensile Strength
σb
ksi 		Yield Point
σs
ksi 		Elongation or Extension Rate
δ
% 		Hardness
HBW
1/4 ~ 1-1/2 (Full-Size) H 110~140 ≥90 HR (C20~30)
1/4 ~ 1-1/2 (Full-Size) HT 160~190 ≥120 HR (C34~45)
1/4 ~ 1-1/2 (Machined) H ≥110 ≥90 ≥18
1/4 ~ 1-1/2 (Machined) HT ≥160 ≥120 ≥12
1 Approximate Comparison Table Martensitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13 4006-410-00-I X10Cr 13
X12Cr 13 		1.4006
1.4006 		Z12C 13
Z10C13 		X12Cr 13 1.4006 12Х13
12KH13
15KH13L 		2302 410S21
2 Approximate Comparison Table Martensitic Heat-Resistant Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13
3
(ISO 683-13-1986) 		X10Cr 13 1.4006 Z12C 13 X12Cr 13 1.4006 12Х13 2302 410S21
3 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
12Cr13
(1Cr13) 		S41010 SUS410 410 S41000 X12Cr13 4006-410-00-I X12Cr13 1.4006

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!