6N01 A 6N01 BE - JIS H 4040-2006

Grade	6N01
Other Names
Corresponding Standard	JIS H 4040-2006 Aluminium and aluminium alloy rods, bars and wires
Classification	Aluminum and Aluminum Alloys

6N01 Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cr	Cu	Ti	Zn	Mg	Other Individual	Other Total	More
Minimum Value	-	0.4	-	-	-	-	-	0.4	-	-	Al:余量；Mn+Cr≤0.5
Maximum Value	0.35	0.9	0.5	0.3	0.35	0.1	0.25	0.8	0.05	0.15	Al:余量；Mn+Cr≤0.5

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

6N01 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Extruded Bar; d ≤ 6	High-Temperature Forming + Artificial Aging (T5)	≥245	≥205	≥8
挤压棒材；6<d≤12	High-Temperature Forming + Artificial Aging (T5)	≥225	≥175	≥8
Extruded Bar; d ≤ 6	Solid Solution Heat Treatment + Artificial Aging (T6)	≥265	≥235	≥8

d: diameter, thickness or width across flats；unit mm
s: cross section area; unit cm²
A、A50mm-gauge length

6N01 Corresponding Standards(Same grade name, different standards)

1	JIS H 4040-2006
	6N01 A 6N01 BE
2	GB /T 3190-2020
	(6N01) 6A01
3	JIS H 4040-2015
	(6N01) 6005C A6005C BE (A6N01 BE)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!