C1700 C1700 P C1700 R - JIS H 3130-2018 - H2ABC

中文版

Grade	C1700
Other Names
Corresponding Standard	JIS H 3130-2018 Copper beryllium alloy, copper titanium alloy, phosphor brozne, copper-nickel-tin alloy and nickel silver sheets, plates and strips for springs
Classification	Copper and Copper Alloys
Properties	Elasticity Corrosion Resistance Fatigue Resistance

C1700 Chemical Element Composition Content (%)

Component	Be	More
Minimum Value	1.6	Cu+Be+Ni+Co+Fe≥99.5；Ni+Co≥0.2；Ni+Co+Fe≤0.6
Maximum Value	1.79	Cu+Be+Ni+Co+Fe≥99.5；Ni+Co≥0.2；Ni+Co+Fe≤0.6

C1700 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Plates (P), Strips (R); 0.10≤t≤1.6	C 1700 P-O,C1700 R-O	Annealing (O)	410~540	-	≥35	HV 90~160
Plates (P), Strips (R); 0.10≤t≤1.6	C 1700 P-1/4H,C1700 R-1/4H	1/4 Hard (1/4H)	510~620	-	≥10	145~220
Plates (P), Strips (R); 0.10≤t≤1.6	C 1700 P-1/2H,C1700 R-1/2H	1/2 Hard (1/2H)	590~695	-	≥5	180~240
Plates (P), Strips (R); 0.10≤t≤1.6	C 1700 P-H,C1700 R-H	Hard (H)	685~835	-	≥2	210~270
Plates (P), Strips (R); 0.10≤t≤1.6	C 1700 P-O,C1700 R-O	Annealing (O)	≥1030	≥890	≥3	≥310
Plates (P), Strips (R); 0.10≤t≤1.6	C 1700 P-1/4H,C1700 R-1/4H	Cold work hardening 1/4 hard (1/4H)	≥1100	≥930	≥2	≥330
Plates (P), Strips (R); 0.10≤t≤1.6	C 1700 P-1/2H,C1700 R-1/2H	Cold work hardening 1/2 hard (1/2H)	≥1180	≥1000	-	≥345
Plates (P), Strips (R); 0.10≤t≤1.6	C 1700 P-H,C1700 R-H	Cold work hardening hard (H)	≥1230	≥1070	-	≥360

Approximate Comparison Table Processing of High Copper Alloys

China		Japan	United States		International Organization for Standardization		Germany		Russia	United Kingdom
GB	ISC	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	GOST	Commercial Grade	BS EN/BS
TBe1.7 QBe1.7	T17700	C1700 C17000	98Cu-1.7Be-.3Co	C17000	CuBe1.7	C17000	CuBe1.7	C17000 2.1245	БрБНТ1.7	CB101	C17000

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!