Home Material ASTM F594-2009(R2015)
简体 | 繁體
Grade F594 304
USA UNS S30400
Corresponding Standard ASTM F594-2009(R2015)
Classification Austenitic Stainless Steel
F594 304 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Cu
Minimum Value - - - - - 18 8 -
Maximum Value 0.08 1 2 0.045 0.03 20 10.5 1
F594 304 Mechanical Properties
Heat Treatment or Condition
Hardness
HBW
1/4 ~ 1-1/2 AF HR（B85 max）
1/4 ~ 1-1/2 A HR（B65~95）
1/4 ~ 5/8 CW1 HR（B95~C35）
3/4 ~ 1-1/2 CW2 HR（B80~C35）
1/4 ~ 5/8 SH1 HR（C24~36）
3/4 ~ 1 SH2 HR（C20~32）
1-1/8 ~ 1-1/4 SH3 HR（B95~C30）
1-3/8 ~ 1-1/2 SH4 HR（B90~C28）
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr19Ni9 S30408 304 SUS 304 STS 304 304 S30400 X5CrNi 18-10 4301-304-00-I X5CrNi 18-10
(X5CrNi 18-9) 		1.4301 Z6CN 18-09 X5CrNi 18-10 1.4301 08Х18Н10 2332
2333 		304S15
2 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr19Ni10
(0Cr18Ni9) 		S30408 304 SUS 304 STS 304 304 S30400 X5CrNi 18-10 X5CrNi 18-10
(X5CrNi 18-9) 		1.4301 Z6CN 18-09 X5CrNi 18-10 1.4301 08Х18Н10 2332
2333 		304S15
3 Approximate Comparison Table Stainless steels for cold heading and cold extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
06Cr19Ni10
(0Cr18Ni9) 		S30408 SUS304 304 S30400 X5CrNi18-10 4301-304-00-I X5CrNi18-10 1.4301

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!