F837 Group 1-CW1 305 S30500 - ASTM F837-2013(R2018)

Grade	F837 Group 1-CW1 305
USA UNS	S30500
Corresponding Standard	ASTM F837-2013(R2018) Stainless steel socket head cap screws
Classification	Austenitic Stainless Steel

F837 Group 1-CW1 305 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu
Minimum Value	-	-	-	-	-	17	10.5	-
Maximum Value	0.12	1	2	0.045	0.03	19	13	1

F837 Group 1-CW1 305 Mechanical Properties

	Tensile Strength σ_b ksi	Yield Point σ_s ksi	Elongation or Extension Rate δ %	Hardness HBW
0.060~0.750 (Full size)	≥102			HRA ≥59
0.060~0.750 (Machined)	≥87	≥65	≥20	≥59

• Core hardness is only required when full-size product tensile testing cannot be accomplished.
• D denotes nominal thread size

1 Approximate Comparison Table

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

Russia

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

BS EN/BS

10Cr18Ni12

S30510

305

SUS 305

STS 305

305

S30500

X6CrNi 18-12

X5CrNi 18-12
(X5CrNi 19-11)
X4CrNi 18-12

1.4303
1.4303

Z8CN 18-12

X4CrNi 18-12

1.4303

12Х18Н12Т

305S19

2 Approximate Comparison Table

China	Japan	United States	International Organization for Standardization		European Standard
ISC	JIS	UNS	ISO	Numerical Grade	Numerical Grade
S38148	SUSXM15J1	S30500	X6CrNiSi18-13-4	4884-305-00-X	(1.4884)

3 Approximate Comparison Table Stainless steels for cold heading and cold extruding

China		Japan	United States		International Organization for Standardization		European Standard
GB	ISC	JIS	ASTM/AISI	UNS	ISO	Numerical Grade	EN	Numerical Grade
10Cr18Ni12 (1Cr18Ni12)	S30510	SUS305	305	S30500	X6CrNi18-12	4303-305-00-I	X6CrNi18-12	1.4303

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!