Grade	C2100
Other Names
Corresponding Standard	JIS H 3100-2018 Copper and copper alloy sheets, plates and strips
Classification	Copper and Copper Alloys
Properties	Corrosion Resistance Machinability

C2100 Chemical Element Composition Content (%)

Component	Fe	Cu	Pb	More
Minimum Value	-	94	-	Zn：余量
Maximum Value	0.05	96	0.03	Zn：余量

C2100 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %	Hardness HBW
Strip (R, RS); 0.3≤t≤3	C2100 R-O,C2100 RS-O	Annealing (O)	≥205	≥33	-
Plate (P); 0.3≤t≤30	C2100 P-O	Annealing (O)	≥205	≥33	-
Plate (P); 0.3≤t≤30	C2100 P-1/4H	1/4 Hard (1/4H)	225~305	≥23	-
Strip (R, RS); 0.3≤t≤3	C2100 R-1/4H,C2100 RS-1/4H	1/4 Hard (1/4H)	225~305	≥23	-
Plates (P); 0.3≤t≤20	C2100 P-1/2H	1/2 Hard (1/2H)	265~345	≥18	-
Strip (R, RS); 0.3≤t≤3	C2100 R-1/2H,C2100 RS-1/2H	1/2 Hard (1/2H)	265~345	≥18	-
Sheet (P); 0.3≤t≤10	C2100 P-H	Hard (H)	≥305	-	-
Strip (R, RS); 0.3≤t≤3	C2100 R-H,C2100 RS-H	Hard (H)	≥305	-	-

Approximate Comparison Table Brass

China	Japan	United States		International Organization for Standardization		Germany		European Standard		Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST
H95	C2100	95Cu-5Zn	C21000	CuZn5	C21000	CuZn5	C21000 2.0220	CuZn5	CW500L	Л96

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!