20Cr1Mo1VA - GB /T 20410-2006

Grade	20Cr1Mo1VA
Corresponding Standard	GB /T 20410-2006 Steels for Turbine Bolts at High Temperature
Classification	Alloy Steel

20Cr1Mo1VA Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	V	Al
Minimum Value	0.15	0.2	0.4	-	-	1	-	-	0.9	0.15	-
Maximum Value	0.23	0.6	0.85	0.025	0.025	1.5	0.3	0.25	1.2	0.3	0.015

20Cr1Mo1VA Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
d=25	Quenching + Tempering	700~850	≥550	≥16	HBW10/3000 210~250	≥69
	High Temperature Tempering				≤241

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!