USA UNS S31653
AISI
American Iron and Steel Institute
316LN
Corresponding Standard SAE J405-2018
Chemical Compositions of SAE Wrought Stainless Steels
Classification Austenitic Stainless Steel
Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Mo N
Minimum Value - - - - - 16 10 2 0.1
Maximum Value 0.03 0.75 2 0.045 0.03 18 14 3 0.16
1 Approximate Comparison Table Austenitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
022Cr17Ni12Mo2N
(00Cr17Ni13Mo2N)
S31653 316LN SUS 316LN STS 316LN 316LN S31653 X2CrNiMoN 17-12-2
X2CrNiMoN 17-11-2
X2CrNiMoN 17-13-3
(X2CrNiMoN 18-13)
1.4429 Z2CND 17-13Az
Z3CND 17-12Az
X2CrNiMoN 17-13-3
X2CrNiMoN 17-12-2
1.4429
1.4406
2375 316S63
316S61
2 Approximate Comparison Table Austenitic Stainless Steel
Japan United States France European Standard United Kingdom
JIS ASTM NF EN/NF EN Numerical Grade BS EN/BS
SUS316LN 316LN Z3CND17-11Az X2CrNiMoN17-11-2 1.4406 316S61
3 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
022Cr17Ni12Mo2N
(00Cr17Ni13Mo2N)
S31653 SUS316LN 316LN S31653 X2CrNiMoN17-12-3 4429-316-53-I X2CrNiMoN17-12-3 1.4429