F468MA Cu 110 C11000 - ASTM F468M-2006(R2012)

Grade	F468MA Cu 110
USA UNS	C11000
Corresponding Standard	ASTM F468M-2006(R2012) Nonferrous Bolts, Hex Cap Screws, and Studs for General Use (Metric)
Classification	Copper and Copper Alloys

F468MA Cu 110 Chemical Element Composition Content (%)

Component	Cu
Minimum Value	99.9
Maximum Value	-

F468MA Cu 110 Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Full-Size	205~345	≥70		HRF 65~90
Machined Specimen	≥205	≥70	≥15	65~90

Note1: Where both tension and hardness tests are performed, the tension tests shall take precedence for acceptance purposes.
Note2: The yield and tensile streng1h values for full-size products shall be computed by dividing the yield and maximum tensile load by the stress area for the product diameter and thread pitch as given in table on tensile stress areas

1 Approximate Comparison Table Processing Pure Copper, Silver Copper

China		Japan	United States		International Organization for Standardization		Germany		France	European Standard	Russia
GB	ISC	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	NF EN/NF	EN	GOST
T2	T11050	C1100 Cu99.90	99.90Cu	C11000	Cu-FRHC	C11000	ECu-57	C11000 2.0090	Cu-FRHC C11000	Cu-FRHC	М1

2 Approximate Comparison Table Processing Pure Copper, Silver Copper

Japan	United States	International Organization for Standardization	Germany		France	European Standard		Russia	Sweden	United Kingdom
JIS	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
C1100	C11000	Cu-ETP	E-Cu58 E2-Cu58	2.0065	CuA1	Cu-ETP	CW004A	M1	5010	C101

3 Approximate Comparison Table Processing Pure Copper, Silver Copper

China	Japan	United States	International Organization for Standardization	Germany	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	BS EN/BS
T2	C1100	C11000	Cu-FRHC	E-Cu58	C101 C102