F468MAB Cu 260 C26000 - ASTM F468M-2006(R2012)

Grade	F468MAB Cu 260
USA UNS	C26000
Corresponding Standard	ASTM F468M-2006(R2012) Nonferrous Bolts, Hex Cap Screws, and Studs for General Use (Metric)
Classification	Copper and Copper Alloys

F468MAB Cu 260 Chemical Element Composition Content (%)

Component	Fe	Cu	Pb	More
Minimum Value	-	68.5	-	Zn:Balance
Maximum Value	0.05	71.5	0.07	Zn:Balance

F468MAB Cu 260 Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Full-Size	410~620	≥345		HRF 55~80
Machined Specimen	≥380	≥345	≥35	55~80

Note1: Where both tension and hardness tests are performed, the tension tests shall take precedence for acceptance purposes.
Note2: The yield and tensile streng1h values for full-size products shall be computed by dividing the yield and maximum tensile load by the stress area for the product diameter and thread pitch as given in table on tensile stress areas

1 Approximate Comparison Table brass

China	Japan	United States		International Organization for Standardization		Germany		European Standard		Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST
H70	C2600	70Cu-30Zn	C26000	CuZn30	C26000	CuZn30	C26000 2.0265	CuZn30	CW505L	Л70

2 Approximate Comparison Table Cupper and cupper alloy

Japan	United States	International Organization for Standardization	Germany		France	European Standard		Russia	Sweden	United Kingdom
JIS	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
C2600	C26000	CuZn30	CuZn30	2.0265	CuZn30	CuZn30	CW505L	L70	CuZn30	CZ106

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!