F468MT Ni 276 N10276 - ASTM F468M-2006(R2012)

Grade	F468MT Ni 276
USA UNS	N10276
Corresponding Standard	ASTM F468M-2006(R2012) Nonferrous Bolts, Hex Cap Screws, and Studs for General Use (Metric)
Classification	Nickel and Nickel Alloys

F468MT Ni 276 Chemical Element Composition Content (%)

Component	Fe	C	Si	Mn	P	S	Cr	Mo	W	V	Co	More
Minimum Value	4	-	-	-	-	-	14.5	15	3	-	-	Ni:Balance
Maximum Value	7	0.02	0.08	1	0.04	0.03	16.5	17	4.5	0.35	2.5	Ni:Balance

F468MT Ni 276 Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Full-Size	760~970	≥310		HRC 20~32
Machined Specimen	≥760	≥310	≥25	20~32

Note1: Where both tension and hardness tests are performed, the tension tests shall take precedence for acceptance purposes.
Note2: The yield and tensile streng1h values for full-size products shall be computed by dividing the yield and maximum tensile load by the stress area for the product diameter and thread pitch as given in table on tensile stress areas

1 Approximate Comparison Table Corrosion-Resistant Alloy

China		United States		Germany		United Kingdom
GB	ISC	Commercial Grade	UNS	DIN EN/DIN	W-Nr.	BS EN/BS
NS 3304 (NS 334) (00Cr15Ni60Mo16W5Fe5)	H10276 (H 03304)	Inconel 276 Inconel C-276	N 10276	NiMo16Cr15W	2.4819	NA 45

2 Approximate Comparison Table Wrought Corrosion-Resistant Alloy for Welding

China		United States		International Organization for Standardization
GB	ISC	ASTM	AWS	ISO
HNS 3304 NiCr15Mo16Fe6W4	W 50276	N 10276	ERNiCrMo-4	SNi 6276

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!