F468MU Ni 400 N04400 - ASTM F468M-2006(R2012)

Grade	F468MU Ni 400
USA UNS	N04400
Corresponding Standard	ASTM F468M-2006(R2012) Nonferrous Bolts, Hex Cap Screws, and Studs for General Use (Metric)
Classification	Nickel and Nickel Alloys

F468MU Ni 400 Chemical Element Composition Content (%)

Component	Fe	C	Si	Mn	S	Ni	More
Minimum Value	-	-	-	-	-	63	Cu:Balance
Maximum Value	2.5	0.3	0.5	2	0.024	70	Cu:Balance

F468MU Ni 400 Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Full-Size, M6~M20	550~900	≥275		75HRB~25HRC
Full-Size, M24~M36	480~900	≥205		60HRB~25HRC
Machined Specimen, M6~M20	≥550	≥275	≥20	75HRB~25HRC
Machined Specimen, M24~M36	≥480	≥205	≥20	60HRB~25HRC

Note1: Where both tension and hardness tests are performed, the tension tests shall take precedence for acceptance purposes.
Note2: The yield and tensile streng1h values for full-size products shall be computed by dividing the yield and maximum tensile load by the stress area for the product diameter and thread pitch as given in table on tensile stress areas

Approximate Comparison Table Corrosion-Resistant Alloy

China		United States		Germany
GB	ISC	Commercial Grade	UNS	DIN EN/DIN	W-Nr.
NS 6400 Ni68Cu28Fe	H 04400	Monel 400	N 04400	NiCu30Fe	2.4360

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!