F468MAT Ti 1 R50250 - ASTM F468M-2006(R2012)

Grade	F468MAT Ti 1
USA UNS	R50250
Corresponding Standard	ASTM F468M-2006(R2012) Nonferrous Bolts, Hex Cap Screws, and Studs for General Use (Metric)
Classification	Titanium and Titanium Alloys

F468MAT Ti 1 Chemical Element Composition Content (%)

Component	Fe	C	N	H	O	Other Individual	Other Total	More
Minimum Value	-	-	-	-	-	-	-	Ti:Balance
Maximum Value	0.2	0.1	0.05	0.0125	0.18	0.1	0.4	Ti:Balance

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

F468MAT Ti 1 Mechanical Properties

	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Full-Size	240~480	≥170		HV 140~160
Machined Specimen	≥240	≥170	≥24	140~160

Note1: Where both tension and hardness tests are performed, the tension tests shall take precedence for acceptance purposes.
Note2: The yield and tensile streng1h values for full-size products shall be computed by dividing the yield and maximum tensile load by the stress area for the product diameter and thread pitch as given in table on tensile stress areas

Approximate Comparison Table Processing titanium and titanium alloy

China	Japan	United States		International Organization for Standardization	Germany		France	Russia
GB	JIS	ASTM	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST
TA1	Class 2 Ti≥99.49	Grade 1	R50250	Grade 1(Ti≥99.53)	Ti2(Ti≥99.50)	3.7035	T-40(Ti≥99.54)	ВТ1-00(Ti99.57)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!