USA UNS S41008
AISI
American Iron and Steel Institute
410S
Corresponding Standard SAE J405-2018
Chemical Compositions of SAE Wrought Stainless Steels
Classification Martensitic Stainless Steel
Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni
Minimum Value - - - - - 11.5 -
Maximum Value 0.08 1 1 0.04 0.03 13.5 0.6
New and Old Grade Replacement List
Corresponding Standard Grade
SAE J405-1998
Grade
USA UNS
SAE J405-2018
USA UNS
AISI
1 Approximate Comparison Table Martensitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade
06Cr13
(0Cr13)
S41008 410S SUS 410S STS 410S 410S S41008 X6Cr 13 X6Cr 13
(X7Cr 13)
1.4000 Z6C 13 X6Cr 13 1.4000
2 Approximate Comparison Table Martensitic Stainless Steel
China Japan United States Germany France European Standard Russia Sweden United Kingdom
GB JIS ASTM UNS DIN EN/DIN NF EN/NF EN Numerical Grade GOST SS BS EN/BS
0Cr13 SUS410S 410S
Type403
S41008 X7Cr14 Z6C13
Z8C12
X6Cr13 1.4000 08KH13 2301 403S17
3 Approximate Comparison Table Ferritic Stainless Steel
China Japan United States International Organization for Standardization European Standard Russia
GB ISC JIS ASTM UNS ISO Numerical Grade EN Numerical Grade GOST
06Cr13
(0Cr13)
GB/T 20878-2024
S11306
(S41008)
SUS410S 410S
ASTM A959
S41008 X6Cr13
ISL 15510
4000-410-08-I X6Cr13
EN 10088-1
1.4000 08Х13
GOST 5632

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!