A600 M33 T11333 - ASTM A600-1992(R2010) - H2ABC

中文版

Grade	A600 M33
USA UNS	T11333
AISI American Iron and Steel Institute	M33
Corresponding Standard	ASTM A600-1992(R2010) Standard Specification for Tool Steel High Speed
Classification	Alloy Steel

A600 M33 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Mo	W	V	Co	More
Minimum Value	0.85	0.15	0.15	-	-	3.5	9	1.3	1	7.75	Ni+Cu≤ 0.75
Maximum Value	0.92	0.5	0.4	0.03	0.03	4	10	2.1	1.35	8.75	Ni+Cu≤ 0.75

A600 M33 Mechanical Properties

	Heat Treatment or Condition	Hardness HBW
Bars, forgings, thick plates, thin plates, strip products	Cold Drawing	HB ≤285
Bars, forgings, thick plates, thin plates, strip products	Cold Drawn and Annealed	≤277
Bars, forgings, thick plates, thin plates, strip products	Annealing	≤269
Bars, forgings, thick plates, thin plates, strip products	Heat Treatment	HR ≥65

Approximate Comparison Table

China	Japan	United States	International Organization for Standardization	Germany		France	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
W2Mo9Cr4VCo8	YXM34	M33 M34	HS2-9-1-8	S2-9-2-8	1.3249	Z110DKCWV09-08-04-02-01	BM34

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!