17CrS3 1.7014 - EN 10263-3-2017

Grade	17CrS3
European Standard Steel Grade	1.7014
Corresponding Standard	EN 10263-3-2017 Steel rod, bars and wire for cold heading and cold extrusion Part 3: Technical delivery conditions for steels for case hardening steels
Classification	Alloy Steel

17CrS3 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Cu
Minimum Value	0.14	-	0.6	-	0.02	0.7	-
Maximum Value	0.2	0.3	0.9	0.025	0.04	1	0.25

17CrS3 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %	Hardness HBW
Bars; 5<d≤40	Processed to Ferrite-Pearlite Structure and Hardness Range (+FP)			140~187
Bars; 5<d≤40	Spheroidizing (+AC)	≤520	≥60
Bar, wire; 2<d≤5	Untreated, Cold Drawn, Spheroidizing Treatment (+U+C+AC)	≤520	≥62
Bar, wire; 5<d≤40	Untreated, Cold Drawn, Spheroidizing Treatment (+U+C+AC)	≤500	≥62
Bar, wire; 2<d≤5	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤560	≥60
Bar, wire; 5<d≤40	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤540	≥60
Bars, wire; 5<d≤10	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤630	≥57
Bars, wire; 10<d≤40	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤620	≥57

1 Approximate Comparison Table structural alloy steel

Japan	International Organization for Standardization	European Standard
JIS	ISO	EN	Numerical Grade
SCR415HRCH	17CrS3	17CrS3	1.7014

2 Approximate Comparison Table

Japan	International Organization for Standardization	European Standard
JIS	ISO	EN	Numerical Grade
SCR415HRCH	17CrS3	17CrS3	1.7014

17CrS3 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!