C15E2C 1.1132 - EN 10263-3-2017

Grade	C15E2C
European Standard Steel Grade	1.1132
Corresponding Standard	EN 10263-3-2017 Steel Rod, Bars and Wire for Cold Heading and Cold Extrusion Part 3: Technical Delivery Conditions for Steels for Case Hardening Steels
Classification	Carbon Steel

C15E2C Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cu
Minimum Value	0.13	-	0.3	-	-	-
Maximum Value	0.17	0.3	0.6	0.025	0.025	0.25

C15E2C Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
Bars, rods, wires; 5<d≤100	Unprocessed or Descaled (+U or +PE)	≤480	≥58
Bars, rods, wires; 5<d≤100	Spheroidizing or Spheroidizing and Peeling (+AC or +AC+PE)	≤430	≥65
Bars, wire; 5<d≤10	Untreated and Cold Drawn (+U+C)	≤570	≥56
Bars, wire; 10<d≤40	Untreated and Cold Drawn (+U+C)	≤560	≥56
Bar, wire; 2<d≤5	Untreated, Cold Drawn, and Spheroidized (+U+C+AC)	≤420	≥67
Bar, wire; 5<d≤40	Untreated, Cold Drawn, and Spheroidized (+U+C+AC)	≤410	≥67
Bar, wire; 2<d≤5	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤460	≥65
Bar, wire; 5<d≤40	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤450	≥65
Bars, wire; 5<d≤10	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤520	≥62
Bars, wire; 10<d≤40	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤510	≥62

1 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China	Japan	South Korea	United States	International Organization for Standardization	Germany	European Standard	United Kingdom
GB	JIS	KS	ASTM	ISO	DIN EN/DIN	EN	BS EN/BS
ML15	SWRCH15K	SWCH15K	1015	CC15A C15GC	QSt38-3	C15E2C	0/3

2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

International Organization for Standardization	European Standard
ISO	EN	Numerical Grade
C15E2C	C15E2C	1.1132

C15E2C Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!