C15E2C 1.1132 - DIN EN 10263-3-2018

Grade	C15E2C
Germany W-Nr.	1.1132
Corresponding Standard	DIN EN 10263-3-2018 Steel rod, bars and wire for cold heading and cold extrusion Part 3: Technical delivery conditions for case hardening steels
Classification	Carbon Steel

C15E2C Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cu
Minimum Value	0.13	-	0.3	-	-	-
Maximum Value	0.17	0.3	0.6	0.025	0.025	0.25

C15E2C Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
Bars, rods, wires; 5<d≤100	Unprocessed or Descaled (+U or +PE)	≤480	≥58
Bars, rods, wires; 5<d≤100	Spheroidizing or Spheroidizing and Peeling (+AC or +AC+PE)	≤430	≥65
Bars, wire; 5<d≤10	Untreated and Cold Drawn (+U+C)	≤570	≥56
Bars, wire; 10<d≤40	Untreated and Cold Drawn (+U+C)	≤560	≥56
Bar, wire; 2<d≤5	Untreated, Cold Drawn, and Spheroidized (+U+C+AC)	≤420	≥67
Bar, wire; 5<d≤40	Untreated, Cold Drawn, and Spheroidized (+U+C+AC)	≤410	≥67
Bar, wire; 2<d≤5	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤460	≥65
Bar, wire; 5<d≤40	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤450	≥65
Bars, wire; 5<d≤10	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤520	≥62
Bars, wire; 10<d≤40	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤510	≥62

Approximate Comparison Table Cold Heading Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ML15

U40152

SWRCH15K

1015

G10150

CC15A
(A4Al)

QSt38-3
(C14C)
Cq15
(C15C)

1.0234
-
1.1132

FR15
FB18
FR18

15nc

0/3

C15E2C Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!