Grade A193 B8C Class 1
USA UNS S34700
Other Names
Corresponding Standard ASTM A193/A193M-2020
Alloy-Steel and Stainless Steel Bolting for High Temperature or High Pressure Service and Other Special Purpose Applications
Classification Austenitic Stainless Steel
Properties Corrosion Resistance Forgability Weldability
A193 B8C Class 1 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni More
Minimum Value - - - - - 17 9 Nb:10C~1.10
Maximum Value 0.08 1 2 0.045 0.03 19 12
• The intentional addition of Bi, Se, Te, and Pb is not permitted
A193 B8C Class 1 Mechanical Properties
diameter
d
mm
Heat Treatment or Condition
Tensile Strength
σb
Mpa
Yield Point
σs
Mpa
Elongation or Extension Rate
δ
%
Reduction of Area
ψ
%
Hardness
HBW
All Sizes Carbide Solid Solution Treatment ≥515 ≥205 ≥30 ≥50 ≤223
• d-diameter of bolt, screw, studs, double-end studs, bars and wire.
1 Approximate Comparison Table Austenitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr18Ni11Nb S34778 347 SUS 347 STS 347 347 S34700 X6CrNiNb 18-10 X6CrNiNb 18-10
(X10CrNiNb18-9)
1.4550 Z6CNNb 18-10 X6CrNiNb 18-10 1.4550 08Х18Н12Б 2338 347S17
347S31
2 Approximate Comparison Table Austenitic Heat-Resistant Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr18Ni11Nb
(0Cr18Ni11Nb)
S34778 347 SUS 347 STS 347 347 S34700 X6CrNiNb 18-10 X6CrNiNb 18-10
(X10CrNiNb18-9)
1.4550 Z6CNNb 18-10 X6CrNiNb 18-10 1.4550 08Х18Н12Б 2338 347S17
347S31
A193B8CClass1 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!