X1CrNiMoCuN 24-22-8 1.4652 - DIN EN 10088-3-2014

Grade	X1CrNiMoCuN 24-22-8
Germany W-Nr.	1.4652
Corresponding Standard	DIN EN 10088-3-2014 Stainless steels – Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
Classification	Austenitic Stainless Steel
Properties	Corrosion Resistance
Density	8 g/cm³

X1CrNiMoCuN 24-22-8 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N
Minimum Value	-	-	2	-	-	23	21	0.3	7	0.45
Maximum Value	0.02	0.5	4	0.03	0.005	25	23	0.6	8	0.55

① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X1CrNiMoCuN 24-22-8 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
Bar, rod, wire, section, bright products; d≤50	+AT	750~1000	≥430	(long.) ≥40	≤310	(long.) ≥100

+AT=solution annealed；+A=annealed；+QT = quenched and tempered；+P=precipitation hardening；+C=Cold worked，+Csuffix followed by a number represents the tensile strength grade, i.e., the minimum tensile strength value.
long.=longitudinal；tr.=transverse
d=diameter or thickness；Unit mm

Approximate Comparison Table Austenitic Stainless Steel

China		United States		International Organization for Standardization		Germany		European Standard
GB	ISC	Commercial Grade	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade
015Cr24Ni22Mo8Mn3CuN 654SMo	S32652	654SMO	S32654	X1CrNiMoCuN24-22-8	4652-326-54-I	X1CrNiMoCuN24-22-8	1.4652	X1CrNiMoCuN24-22-8	1.4652

X1CrNiMoCuN24-22-8 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X1CrNiMoCuN 24-22-8 1.4652
2	ISO TS 15510-2003
	X1CrNiMoCuN24-22-8
3	EN 10088-3-2014
	X1CrNiMoCuN 24-22-8 1.4652
4	ISO 15510-2014
	X1CrNiMoCuN24-22-8 4652-326-54-I
5	DIN EN 10088-3-2014
	X1CrNiMoCuN 24-22-8 1.4652
6	NF EN 10088-2-2005
	X1CrNiMoCuN24-22-8 1.4652
7	NF EN 10088-1-2005
	X1CrNiMoCuN24-22-8 1.4652

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!