C20E2C 1.1152 - DIN EN 10263-3-2018

Grade	C20E2C
Germany W-Nr.	1.1152
Corresponding Standard	DIN EN 10263-3-2018 Steel rod, bars and wire for cold heading and cold extrusion Part 3: Technical delivery conditions for case hardening steels
Classification	Carbon Steel

C20E2C Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cu
Minimum Value	0.18	-	0.3	-	-	-
Maximum Value	0.22	0.3	0.6	0.025	0.025	0.25

C20E2C Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
Bars, rods, wires; 5<d≤100	Unprocessed or Descaled (+U or +PE)	≤530	≥58
Bars, rods, wires; 5<d≤100	Spheroidizing or Spheroidizing and Peeling (+AC or +AC+PE)	≤470	≥65
Bars, wire; 5<d≤10	Untreated and Cold Drawn (+U+C)	≤640	≥56
Bars, wire; 10<d≤40	Untreated and Cold Drawn (+U+C)	≤630	≥56
Bar, wire; 2<d≤5	Untreated, Cold Drawn, and Spheroidized (+U+C+AC)	≤460	≥67
Bar, wire; 5<d≤40	Untreated, Cold Drawn, and Spheroidized (+U+C+AC)	≤450	≥67
Bar, wire; 2<d≤5	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤500	≥65
Bar, wire; 5<d≤40	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤490	≥65
Bars, wire; 5<d≤10	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤580	≥62
Bars, wire; 10<d≤40	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤570	≥62

Approximate Comparison Table

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ML20

U40202

SWRCH20K

1020

G10200

CC21A
(A5Al)

Cq22
(C22C)

1.1152

XC18
FR20

20nc

0/4

C20E2C Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!