16MnCrS 5 1.7139 - DIN EN 10263-3-2018

Grade	16MnCrS 5
Germany W-Nr.	1.7139
Corresponding Standard	DIN EN 10263-3-2018 Steel rod, bars and wire for cold heading and cold extrusion Part 3: Technical delivery conditions for case hardening steels
Classification	Alloy Steel

16MnCrS 5 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Cu
Minimum Value	0.14	-	1	-	0.02	0.8	-
Maximum Value	0.19	0.3	1.3	0.025	0.04	1.1	0.25

16MnCrS 5 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %	Hardness HBW
Bars; 5<d≤40	Processed to Ferrite-Pearlite Structure and Hardness Range (+FP)			140~187
Bars; 5<d≤40	Spheroidizing (+AC)	≤550	≥62
Bar, wire; 2<d≤5	Untreated, Cold Drawn, Spheroidizing Treatment (+U+C+AC)	≤550	≥64
Bar, wire; 5<d≤40	Untreated, Cold Drawn, Spheroidizing Treatment (+U+C+AC)	≤530	≥64
Bar, wire; 2<d≤5	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤590	≥62
Bar, wire; 5<d≤40	Untreated, Cold Drawn, Spheroidizing Treatment, and Tempered Rolling (+U+C+AC+LC)	≤570	≥62
Bars, wire; 5<d≤10	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤660	≥59
Bars, wire; 10<d≤40	Spheroidizing Treatment and Cold Drawing (+AC+C)	≤650	≥59

Approximate Comparison Table Structural Alloy Steel

International Organization for Standardization	Germany	France	European Standard		Sweden
ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	SS
16MnCrS5	16MnCrS5	16MC5	16MnCrS5	1.7139	2127

16MnCrS5 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!