X12CrMnNiN17-7-5 4372-201-00-I - ISO 15510-2014

Grade	X12CrMnNiN17-7-5
ISO Numeric Designation	4372-201-00-I
Corresponding Standard	ISO 15510-2014 TECHNICAL SPECIFICATION Stainless steels-Chemical composition
Classification	Austenitic Stainless Steel

X12CrMnNiN17-7-5 Chemical Element Composition Content (%)

Component	C ^①	Si	Mn	P	S ^②	Cr	Ni	N
Minimum Value	-	-	5.5	-	-	16	3.5	0.05
Maximum Value	0.15	1	7.5	0.045	0.03	18	5.5	0.25

① Particular ranges of sulfur mass fraction can provide improvement of particular properties. For machinability, a controlled sulfur mass fraction of 0.015% to 0.03% is recommended. For weldability, a controlled sulfur mass fraction of 0.008% to 0.02% can be beneficial. For polishability, a controlled sulfur mass fraction of 0.015% maximum is recommeded.
② For pressure purposes, a carbon limit of C ≤0.07% is allowed.

Approximate Comparison Table

China	Japan	United States	International Organization for Standardization		European Standard
ISC	JIS	UNS	ISO	Numerical Grade	Numerical Grade
S35350	SUS201	S20100	X12CrMnNiN17-7-5	4372-201-00-I	1.4372

X12CrMnNiN17-7-5 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X12CrMnNiN 17-7-5 1.4372
2	ISO TS 15510-2003
	X12CrMnNiN17-7-5
3	EN 10088-3-2014
	X12CrMnNiN 17-7-5 1.4372
4	ISO 15510-2014
	X12CrMnNiN17-7-5 4372-201-00-I
5	DIN EN 10088-3-2014
	X12CrMnNiN 17-7-5 1.4372
6	NF EN 10088-2-2005
	X12CrMnNiN17-7-5 1.4372
7	NF EN 10088-1-2005
	X12CrMnNiN17-7-5 1.4372
8	DIN EN 10151-2002
	X12CrMnNiN17-7-5 1.4372