Grade
C10C
European Standard Steel Grade
1.0214
Corresponding Standard
EN 10263-2-2017
Classification
Carbon Steel
C10C Chemical Element Composition Content (%)
Component
C
Si ①
Mn
P
S
Al ②
Minimum Value
0.08
-
0.3
-
-
0.02
Maximum Value
0.12
0.1
0.5
0.025
0.025
0.06
C10C Mechanical Properties
condition
Heat Treatment or Condition
Tensile Strengthb Mpa
Reduction of Area%
Coil, Steel Bar; 5<d≤100
Hot Rolled or Untreated and Pickled (+U or +U+PE)
≤430
≥60
Coil, steel bar; 5 < d ≤ 100
Spheroidizing Annealing or Spheroidizing Annealing + Descaling (+AC or +AC+PE)
≤380
≥70
Steel bar, wire; 5 < d ≤ 10
Untreated and Cold Drawn (+U+C)
≤520
≥58
Steel bar, wire; 10 < d ≤ 40
Untreated and Cold Drawn (+U+C)
≤510
≥58
Steel rods, steel wires; 2＜d≤5
Untreated, Cold Drawn, and Spheroidized (+U+C+AC)
≤370
≥72
Steel bars, steel wires; 5＜d≤40
Untreated, Cold Drawn, and Spheroidized (+U+C+AC)
≤360
≥72
Coil bars, steel bars; 2＜d≤5
Untreated, Cold Drawn, Spheroidized, and Flattened (+U+C+AC+LC)
≤410
≥68
Coiled bars, steel bars; 5＜d≤40
Untreated, Cold Drawn, Spheroidized, and Flattened (+U+C+AC+LC)
≤400
≥68
Steel bar, wire; 5 < d ≤ 10
Spheroidized Annealing and Cold Drawing (+AC+C)
≤470
≥63
Steel bar, wire; 10 < d ≤ 40
Spheroidized Annealing and Cold Drawing (+AC+C)
≤460
≥63
1 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion
Japan
International Organization for Standardization
European Standard
JIS
ISO
EN
Numerical Grade
SWRCH10A
C10C
C10C
1.0214
2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion
3 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion
4 Approximate Comparison Table High-Quality Carbon Structural Steel
C10C Corresponding Standards(Same grade name, different standards)
Message
I want to correct it
Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!