C10C 1.0214 - EN 10263-2-2001

Grade	C10C
European Standard Steel Grade	1.0214
Corresponding Standard	EN 10263-2-2001 Steel Rod,bars and Wire for Cold Heading and Cold Extrusion - Part 2: Technical Delivery Conditions for Steels Not Intended for Heat Treatment after Cold Working
Classification	Carbon Steel

C10C Chemical Element Composition Content (%)

Component	C	Si ^①	Mn	P	S	Al ^②
Minimum Value	0.08	-	0.3	-	-	0.02
Maximum Value	0.12	0.1	0.5	0.025	0.025	0.06

C10C Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
5＜d≤100	+U or +U+PE	≤430	≥60
5＜d≤100	+AC or +AC+PE	≤380	≥70
5＜d≤10	+U+C	≤520	≥58
10＜d≤40	+U+C	≤510	≥58
2＜d≤5	+U+C+AC	≤370	≥72
5＜d≤40	+U+C+AC	≤360	≥72
2＜d≤5	+U+C+AC+LC	≤410	≥68
5＜d≤40	+U+C+AC+LC	≤400	≥68
5＜d≤10	+AC+C	≤470	≥63
10＜d≤40	+AC+C	≤460	≥63

1 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

Japan	International Organization for Standardization	European Standard
JIS	ISO	EN	Numerical Grade
SWRCH10A	C10C	C10C	1.0214

2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN	Numerical Grade
ML10Al	U40108	SWRCH10A	1010	CC11A C10C	C10C	1.0214

3 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN	Numerical Grade
ML10	U40102	SWRCH10K	1010	CC11A C10GC	C10C	1.0214

4 Approximate Comparison Table High-Quality Carbon Structural Steel

5 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
YB	GB	JIS	ASTM	ISO	EN
QML10Al	ML10Al	SWRCH10A	1010	C10C	C10C

C10C Corresponding Standards(Same grade name, different standards)