C1020 C1020 P C1020 PS - JIS H 3100-2018

Grade	C1020
Other Names
Corresponding Standard	JIS H 3100-2018 Copper and copper alloy sheets, plates and strips
Classification	Copper and Copper Alloys

C1020 Chemical Element Composition Content (%)

Component	Cu
Minimum Value	99.96
Maximum Value	-

C1020 Mechanical Properties

condition	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %	Hardness HBW
Plates (P, PS); 0.1 ≤ t < 0.15	C1020 P-O，C1020 P-O	Annealing (O)	≥195	≥20	-
Plate (P, PS); 0.15 ≤ t < 0.3		Annealing (O)	≥195	≥30	-
Plates (P, PS); 0.3≤t≤30		Annealing (O)	≥195	≥35	-
Strips (R, RS); 0.1 ≤ t < 0.15	C1020 R-O，C1020 RS-O	Annealing (O)	≥195	≥20	-
Strip (R, RS); 0.15 ≤ t < 0.3		Annealing (O)	≥195	≥30	-
Strip (R, RS); 0.3≤t≤4		Annealing (O)	≥195	≥35	-
Plates (P, PS); 0.1 ≤ t < 0.15	C1020 P-1/4H，C1020 P-1/4H	1/4 Hard (1/4H)	215~285	≥15	-
Plate (P, PS); 0.15 ≤ t < 0.3		1/4 Hard (1/4H)	215~285	≥20	-
Plates (P, PS); 0.3≤t≤30		1/4 Hard (1/4H)	215~275	≥25	HV 55~100
Strips (R, RS); 0.1 ≤ t < 0.15	C1020 R-1/4H，C1020 RS-1/4H	1/4 Hard (1/4H)	215~285	≥15	-
Strip (R, RS); 0.15 ≤ t < 0.3		1/4 Hard (1/4H)	215~285	≥20	-
Strip (R, RS); 0.3≤t≤4		1/4 Hard (1/4H)	215~275	≥25	55~100
Plates (P, PS); 0.1 ≤ t < 0.15	C1020 P-1/2H，C1020 P-1/2H	1/2 Hard (1/2H)	235~315	-	-
Plate (P, PS); 0.15 ≤ t < 0.3		1/2 Hard (1/2H)	235~315	≥10	* 75~120
Plate material (P, PS); 0.3≤t≤20		1/2 Hard (1/2H)	245~315	≥15	75~120
Strips (R, RS); 0.1 ≤ t < 0.15	C1020 R-1/2H，C1020 RS-1/2H	1/2 Hard (1/2H)	235~315	-	-
Strip (R, RS); 0.15 ≤ t < 0.3		1/2 Hard (1/2H)	235~315	≥10	* 75~120
Strip (R, RS); 0.3≤t≤4		1/2 Hard (1/2H)	245~315	≥15	75~120
Plates (P, PS); 0.1 ≤ t ≤ 10	C1020 P-H，C1020 P-H	Hard (H)	≥275	-	* ≥80
Strip (R, RS); 0.3≤t≤4	C1020 R-H，C1020 RS-H	Hard (H)	≥275	-	≥80

1 Approximate Comparison Table Processing Pure Copper, Silver Copper

China

Japan

United States

International Organization for Standardization

Germany

France

European Standard

Russia

ISC

JIS

ASTM

UNS

ISO

Numerical Grade

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

T10900

C1020
Cu99.96

99.95Cu

C10200

Cu-HPC

C10200

Cu-HPC

C10200

Cu-HPC
C10200

Cu-HPC

CW021

М0б

2 Approximate Comparison Table Copper and Copper Alloy

China	Japan	United States	International Organization for Standardization	Germany	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	BS EN/BS
TU2	C1020	C10200	Cu-OF	OF-Cu	103

C1020 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!