中文版
Home Material EN 12166-1998
简体 | 繁體
Grade CuNi2Si
European Standard Steel Grade CW111C
Corresponding Standard EN 12166-1998
Classification Copper and Copper Alloys
Density 8.8 g/cm3
CuNi2Si Chemical Element Composition Content (%)
Component Fe Si Mn Ni Pb Other Total More
Minimum Value - 0.4 - 1.6 - - Cu:余量
Maximum Value 0.2 0.8 0.1 2.5 0.02 0.3
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
CuNi2Si Mechanical Properties
diameter③
d
mm		 Mark
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
1.5≤d≤6 CuNi2Si-R480 Solution heat treatment + cold working R480 ≥480 ≈450* ≥4*(A100)
≥5(A11.3)
1.5≤d≤6 CuNi2Si-H140 Solution heat treatment + cold working H140 HV: 140~180
6<d≤15 CuNi2Si-R410 Solid Solution + Cold Working R410 ≥410 ≈400* ≥6(A11.3)
≥8(A)
6<d≤15 CuNi2Si-H130 Solid Solution + Cold Working H130 HV: 130~170
1.5≤d≤6 CuNi2Si-R700 Solution heat treatment + cold working + precipitation hardening R700 ≥700 ≈680* ≥6(A100)
≥7(A11.3)
1.5≤d≤6 CuNi2Si-H200 Solution heat treatment + cold working + precipitation hardening H200 HV: 200~250
6<d≤15 CuNi2Si-R640 Solution heat treatment + cold working + precipitation hardening R640 ≥640 ≈620* ≥8(A11.3)
≥10(A)
6<d≤15 CuNi2Si-H190 Solid Solution + Cold Working + Precipitation Hardening H190 HV: 190~240
All specifications CuNi2Si-M M No specification No specification No specification No specification
①Material condition designation: H-Hardness (Brinell or Vickers), the suffix number indicates the hardness value; R-Tensile strength, the suffix number indicates the minimum tensile strength; M-As manufactured, without specified mechanical properties
②A100, A11.3, A-gauge length
③Or equivalent cross-sectional area for polygonal wire.
1 Approximate Comparison Table bronze
China Japan United States International Organization for Standardization European Standard Russia
GB JIS ASTM UNS ISO Numerical Grade EN Numerical Grade GOST
QSi0.6-2 C6470
C64700 		97.5Cu-2Ni-.5Si C64700 CuNi2Si C64700 CuNi2Si CW111C БрКН0.6-2
2 Approximate Comparison Table Cupper and cupper alloy
Germany European Standard
DIN EN/DIN W-Nr. EN Numerical Grade
CuNi2Si 2.0855 CuNi2Si CW111C
CuNi2Si Corresponding Standards(Same grade name, different standards)
1 EN 12163-1998
CuNi2Si CW111C
2 EN 12166-1998
CuNi2Si CW111C
3 EN 1654-1998
CuNi2Si CW111C
4 EN 12166-2016
CuNi2Si CW111C
5 DIN 17672-1-1983
CuNi2Si 2.0855
6 DIN EN 12163-1998
CuNi2Si CW111C (2.0855)
7 DIN EN 12163-2016
CuNi2Si CW111C
8 DIN EN 12166-2016
CuNi2Si CW111C
9 DIN EN 12166-1998
CuNi2Si CW111C
10 DIN 17666-1983
CuNi2Si 2.0855
11 EN 12163-2016
CuNi2Si CW111C
12 EN 12167-2024
CuNi2Si CW111C
13 DIN EN 12449-2019
CuNi2Si CW111C
14 EN 12449-2023
CuNi2Si CW111C

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!