Home Material GB /T 41157.3-2022
简体 | 繁體
Grade 06Cr17Ni12Mo2
China ISC 316
Corresponding Standard GB /T 41157.3-2022
Fasteners for nuclear power plants— Part3: Bolts, screws and studs made of corrosion-resistant stainless steel
Classification Austenitic Stainless Steel
06Cr17Ni12Mo2 Chemical Element Composition Content (%)
Component C Si Mn P ① S ① Cr Ni Mo
Minimum Value - - - - - 16 10 2
Maximum Value 0.08 1 2 0.03 0.015 19 14 2.5
06Cr17Ni12Mo2 Mechanical Properties
product Test Temperature Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW 		Impact Energy Absorption
KV2
J
Bolts, Screws, Studs Room Temperature Solid Solution Treatment ≥520 ≥210 ≥0.6d HBW: 126~192
HRC: 60~90
HV: 127~196		 -
Bolts, Screws, Studs Solid Solution Treatment ≥130
Bolts, screws, studs; d≤20 Room Temperature Unprocessed Work-Hardening ≥760 ≥655 ≥0.3d HBW: ≤320
HRC: ≤35
HV: ≤334		 ≥50
Bolts, screws, studs; 20<d≤24 Room Temperature Unprocessed Work-Hardening ≥690 ≥550 ≥0.4d HBW: ≤320
HRC: ≤35
HV: ≤334		 ≥50
Bolts, screws, studs; 24<d≤33 Room Temperature Unprocessed Work-Hardening ≥655 ≥450 ≥0.4d HBW: ≤320
HRC: ≤35
HV: ≤334		 ≥50
Bolts, screws, studs; 33<d≤39 Room Temperature Unprocessed Work-Hardening ≥620 ≥350 ≥0.4d HBW: ≤320
HRC: ≤35
HV: ≤334		 ≥50
Bolts, screws, studs; d≤20 Unprocessed Work-Hardening ≥510
Bolts, screws, studs; 20<d≤24 Unprocessed Work-Hardening ≥440
Bolts, screws, studs; 24<d≤33 Unprocessed Work-Hardening ≥350
Bolts, screws, studs; 33<d≤39 Unprocessed Work-Hardening ≥270
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
06Cr17Ni12Mo2 S31608 316 SUS 316 STS 316 316 S31600 X5CrNiMo 17-12-2 4401-316-00-I X5CrNiMo 17-12-2
(X5CrNiMo 18-10)
X5CrNiMo 17-13-3
(X5CrNiMo 18-12) 		1.4401
1.4401
1.4436
1.4436 		Z6CND 17-11
Z6CND 17-12 		X5CrNiMo 17-12-2
X3CrNiMo 17-13-3 		1.4401
1.4436 		2347
2343 		316S16
316S31
2 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr17Ni12Mo2
(0Cr17Ni12Mo2)
0Cr18Ni12Mo2Ti 		S31608 316 SUS 316 STS 316 316 S31600 X5CrNiMo 17-12-2 X5CrNiMo 17-12-2
(X5CrNiMo 18-10)
X5CrNiMo 17-13-3
(X5CrNiMo 18-12) 		1.4401
1.4401
1.4436
1.4436 		Z6CND 17-11
Z6CND 17-12 		X5CrNiMo 17-12-2
X3CrNiMo 17-13-3 		1.4401
1.4436 		08Х17Н13М2Т 2347
2343 		316S16
316S31
3 Approximate Comparison Table Stainless steels for cold heading and cold extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
06Cr17Ni12Mo2
(0Cr17Ni12Mo2) 		S31608 SUS316 316 S31600 X5CrNiMo17-12-2 4401-316-00-I X5CrNiMo17-12-2 1.4401
4 Approximate Comparison Table Stainless steels for cold heading and cold extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
06Cr17Ni12Mo2
(0Cr17Ni12Mo2) 		S31608 SUS316 316 S31600 X3CrNiMo17-12-3 4436-316-00-I X3CrNiMo17-12-3 1.4436
06Cr17Ni12Mo2 Corresponding Standards(Same grade name, different standards)
1 GB /T 20878-2007
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2) 316 SS316
2 GB /T 1221-2007
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2) 316 SS316
3 GB /T 1220-2007
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2)
4 GB /T 4240-2019
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2)
5 GB /T 4356-2016
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2) 316 SS316
6 GB /T 3280-2015
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2)
7 GB /T 4238-2015
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2) 316 SS316
8 GB /T 4237-2015
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2)
9 GB /T 14975-2012
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2)
10 GB /T 12770-2012
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2)
11 GB /T 14976-2012
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2)
12 GB /T 12771-2019
06Cr17Ni12Mo2 S31608 SS316
13 YB /T 5363-2016
06Cr17Ni12Mo2 S31608 SS316
14 GB /T 24588-2019
06Cr17Ni12Mo2 S31608 316 SS316
15 GB /T 41157.3-2022
06Cr17Ni12Mo2 316
16 Q/YT 102-2019
06Cr17Ni12Mo2 316
17 GB /T 24511-2017
06Cr17Ni12Mo2 S31608
18 GB /T 20878-2024
06Cr17Ni12Mo2 S31608 (0Cr17Ni12Mo2)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!