Grade 06Cr13
China ISC S11306
Corresponding Standard GB /T 24511-2017
Stainless steel and heat resisting steel plate, sheet and strip for pressure equipments
Classification Duplex Stainless Steel
Density 7.75 g/cm3
06Cr13 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni
Minimum Value - - - - - 11.5 -
Maximum Value 0.08 1 1 0.035 0.02 13.5 0.6
06Cr13 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW
Steel: Annealing Treatment ≥415 ≥205 ≥20
①		 HBW：≤183
HRB：≤89
HV：≤200
1 Approximate Comparison Table Martensitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade
06Cr13
(0Cr13) 		S41008 410S SUS 410S STS 410S 410S S41008 X6Cr 13 X6Cr 13
(X7Cr 13) 		1.4000 Z6C 13 X6Cr 13 1.4000
2 Approximate Comparison Table Ferritic Stainless Steel
China Japan United States International Organization for Standardization European Standard Russia
GB ISC JIS ASTM UNS ISO Numerical Grade EN Numerical Grade GOST
06Cr13
(0Cr13)
GB/T 20878-2024 		S11306
(S41008) 		SUS410S 410S
ASTM A959 		S41008 X6Cr13
ISL 15510 		4000-410-08-I X6Cr13
EN 10088-1 		1.4000 08Х13
GOST 5632
06Cr13 Corresponding Standards(Same grade name, different standards)
1 GB /T 20878-2007
06Cr13 S41008 (0Cr13)
2 GB /T 1220-2007
06Cr13 S41008 (0Cr13)
3 GB /T 4240-2019
06Cr13 S41008
4 GB /T 4356-2016
06Cr13 S41008 (0Cr13)
5 GB /T 3280-2015
06Cr13 S41008 (0Cr13)
6 GB /T 4237-2015
06Cr13 S41008 (0Cr13)
7 GB /T 14975-2012
06Cr13 S41008 (0Cr13)
8 GB /T 12770-2012
06Cr13 S41008 (0Cr13)
9 GB /T 14976-2012
06Cr13 S41008 (0Cr13)
10 GB /T 24511-2017
06Cr13 S11306
11 GB /T 20878-2024
06Cr13 S11306 (0Cr13) (S41008)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!