Home Material EN 10263-5-2017
简体 | 繁體
Grade X12Cr13
European Standard Steel Grade 1.4006
Corresponding Standard EN 10263-5-2017
Steel rod, bars and wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels
Classification Martensitic Stainless Steel
Properties Corrosion Resistance
Density 7.7 g/cm3
X12Cr13 Chemical Element Composition Content (%)
Component C Si Mn P S ⓑ Cr Ni
Minimum Value 0.08 - - - - 11.5 -
Maximum Value 0.15 1 1.5 0.04 0.03 13.5 0.75
X12Cr13 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Rod, Wire; 2<d≤5 Softening Annealing + Cold Drawn + Softening Annealing (+A+C+A) ≤600 ≥60
Wire; 2<d≤5 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤660 ≥58
Bar stock, rod stock, wire; 5 < d ≤ 10 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤600 ≥60
Wire; 5<d≤10 Softening Annealing + Quenching + Softening Annealing (+A+LC) ≤720 ≥57
Rod, Wire; 5<d≤10 Softening Annealing + Cold Drawn + Softening Annealing (+A+C+A) ≤600 ≥60
Wire; 5<d≤10 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤640 ≥58
Bar stock, rod stock, wire stock; 10 < d ≤ 25 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤600 ≥60
Wires; 10<d≤25 Softening Annealing + Quenching + Softening Annealing (+A+LC) ≤700 ≥57
Wires; 10<d≤25 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤600 ≥60
Bars, Rods, Wire; 25<d≤100 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤600 ≥60
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13 4006-410-00-I X10Cr 13
X12Cr 13 		1.4006
1.4006 		Z12C 13
Z10C13 		X12Cr 13 1.4006 12Х13
12KH13
15KH13L 		2302 410S21
2 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13
3
(ISO 683-13-1986) 		X10Cr 13 1.4006 Z12C 13 X12Cr 13 1.4006 12Х13 2302 410S21
3 Approximate Comparison Table Stainless steels for cold heading and cold extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
12Cr13
(1Cr13) 		S41010 SUS410 410 S41000 X12Cr13 4006-410-00-I X12Cr13 1.4006
X12Cr13 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X12Cr 13 1.4006
2 EN 10263-5-2001
X12Cr13 1.4006
3 EN 10250-4-1999
X12Cr 13 1.4006
4 ISO TS 15510-2003
X12Cr13
5 EN 10088-3-2005
X12Cr 13 1.4006
6 EN 10088-3-2014
X12Cr 13 1.4006
7 ISO 15510-2014
X12Cr13 4006-410-00-I
8 DIN EN 10263-5-2018
X12Cr13 1.4006
9 DIN EN 10088-3-2014
X12Cr 13 1.4006
10 ISO 683-18-2014
X12Cr13 4006-410-00-I
11 ISO 4954-2018
X12Cr13 4006-410-00-I
12 NF EN 10088-2-2005
X12Cr13 1.4006
13 NF EN 10088-1-2005
X12Cr13 1.4006
14 DIN EN ISO 7153-1-2016
X12Cr 13 1.4006
15 EN 10263-5-2017
X12Cr13 1.4006
16 ISO 4954-2-2024
X12Cr13 4006-410-00-I

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!