Grade X12Cr 13
European Standard Steel Grade 1.4006
Corresponding Standard EN 10088-1-2005
Staehle Stainless steels. Part 1:List of stainless steels
Classification Martensitic Stainless Steel
Properties Corrosion Resistance
Density 7.7 g/cm3
X12Cr 13 Chemical Element Composition Content (%)
Component C ⓒ Si Mn P S ⓑ Cr Ni
Minimum Value 0.08 - - - - 11.5 -
Maximum Value 0.15 1 1.5 0.04 0.015 13.5 0.75
① Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.
X12Cr 13 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Rod, Wire; 2<d≤5 Soft annealing + cold drawing + soft annealing (+A+C+A) ≤600 ≥60
Wire; 2<d≤5 Soft annealing + Cold drawing + Soft annealing + Quenching rolling (+A+C+A+LC) ≤660 ≥58
Bar stock, rod stock, wire; 5 < d ≤ 10 Soft annealing (+A) or soft annealing + descaling (+A+PE) ≤600 ≥60
Wire; 5<d≤10 Soft annealing + Quenching rolling (+A+LC) ≤720 ≥57
Rod, Wire; 5<d≤10 Soft annealing + cold drawing + soft annealing (+A+C+A) ≤600 ≥60
Wire; 5<d≤10 Soft annealing + Cold drawing + Soft annealing + Quenching rolling (+A+C+A+LC) ≤640 ≥57
Bar stock, rod stock, wire stock; 10 < d ≤ 25 Soft annealing (+A) or soft annealing + descaling (+A+PE) ≤600 ≥60
Wires; 10<d≤25 Soft annealing + Quenching rolling (+A+LC) ≤700 ≥57
Rod, Wire; 10<d≤25 Soft annealing + cold drawing + soft annealing (+A+C+A) ≤600 ≥60
Bars, Rods, Wire; 25<d≤100 Soft annealing (+A) or soft annealing + descaling (+A+PE) ≤600 ≥60
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13 4006-410-00-I X10Cr 13
X12Cr 13 		1.4006
1.4006 		Z12C 13
Z10C13 		X12Cr 13 1.4006 12Х13
12KH13
15KH13L 		2302 410S21
2 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13
3
(ISO 683-13-1986) 		X10Cr 13 1.4006 Z12C 13 X12Cr 13 1.4006 12Х13 2302 410S21
3 Approximate Comparison Table Stainless steels for cold heading and cold extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
12Cr13
(1Cr13) 		S41010 SUS410 410 S41000 X12Cr13 4006-410-00-I X12Cr13 1.4006
X12Cr13 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X12Cr 13 1.4006
2 EN 10263-5-2001
X12Cr13 1.4006
3 EN 10250-4-1999
X12Cr 13 1.4006
4 ISO TS 15510-2003
X12Cr13
5 EN 10088-3-2005
X12Cr 13 1.4006
6 EN 10088-3-2014
X12Cr 13 1.4006
7 ISO 15510-2014
X12Cr13 4006-410-00-I
8 DIN EN 10263-5-2018
X12Cr13 1.4006
9 DIN EN 10088-3-2014
X12Cr 13 1.4006
10 ISO 683-18-2014
X12Cr13 4006-410-00-I
11 ISO 4954-2018
X12Cr13 4006-410-00-I
12 NF EN 10088-2-2005
X12Cr13 1.4006
13 NF EN 10088-1-2005
X12Cr13 1.4006
14 DIN EN ISO 7153-1-2016
X12Cr 13 1.4006
15 EN 10263-5-2017
X12Cr13 1.4006
16 ISO 4954-2-2024
X12Cr13 4006-410-00-I

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!