Grade SWRCH35K
Corresponding Standard JIS G 3507-1-2021
Carbon Steels for Cold Heading - Part 1: Wire Rods
Brand/Supplier
Japan -> JFE Steel
Classification Carbon Steel
Properties Good Forgability
SWRCH35K Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Cu
Minimum Value 0.32 0.1 0.6 - - - - -
Maximum Value 0.38 0.35 0.9 0.03 0.035 0.2 0.2 0.3
1 Approximate Comparison Table Cold Heading Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France Russia United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ML35 U40352 SWRCH35K SWRCH35K SWRCH35K 1034 G10340 CE35E4
(C3) 		Cq35
(C35C) 		1.1172 XC38
FR36 		35 1/2
2 Approximate Comparison Table Cold Heading Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization France United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO NF EN/NF BS EN/BS
ML35Mn U41352 SWRCH38K SWRCH35K
SWRCH38K 		SWRCH35K 1034 G10340 CE35E4 1C35 2/1
3 Approximate Comparison Table High-Quality Carbon Structural Steel
China Japan United States Germany France Russia United Kingdom
GB JIS ASTM/AISI DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
35Mn
(GB/T 699-1999) 		SWRCH35K 1037 C35 1.0501 C35 35Г 080A35
080A36
C35
4 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion
China Japan United States International Organization for Standardization European Standard
YB GB JIS ASTM ISO EN
QML35 ML35 SWRCH35K 1035 C35EC C35EC
SWRCH35K Corresponding Standards(Same grade name, different standards)
1 JIS
SWRCH35K
2 JIS G 3507-1-2005
SWRCH35K 35K
3 Q/BQB 517-2018
SWRCH35K
4 JIS G 3507-1-2010
SWRCH35K
5 Q/ASB 325-2004
SWRCH35K
6 Q/ASB 234-2018
SWRCH35K
7 Q/XG 114-2016
SWRCH35K
8 JIS G 3507-1-2021
SWRCH35K

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!