SWRCH35K 35K - JIS G 3507-1-2005

Grade	SWRCH35K
Other Names
Corresponding Standard	JIS G 3507-1-2005 Carbon Steels for Cold Heading - Part 1: Wire Rods
Classification	Carbon Steel

SWRCH35K Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S
Minimum Value	0.32	0.1	0.6	-	-
Maximum Value	0.38	0.35	0.9	0.03	0.035

SWRCH35K Mechanical Properties

Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %
(Reference value) ≤620	Cross-sectional shrinkage rate ψ% (Reference value) ≥45

1 Approximate Comparison Table Cold Heading Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ML35

U40352

SWRCH35K

1034

G10340

CE35E4
(C3)

Cq35
(C35C)

1.1172

XC38
FR36

1/2

2 Approximate Comparison Table Cold Heading Steel

China		Taiwan, China	Japan	South Korea	United States		International Organization for Standardization	France	United Kingdom
GB	ISC	CNS	JIS	KS	ASTM/AISI	UNS	ISO	NF EN/NF	BS EN/BS
ML35Mn	U41352	SWRCH38K	SWRCH35K SWRCH38K	SWRCH35K	1034	G10340	CE35E4	1C35	2/1

3 Approximate Comparison Table High-Quality Carbon Structural Steel

SWRCH35K Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!