C8C 1.0213 - EN 10263-2-2001

Grade	C8C
European Standard Steel Grade	1.0213
Corresponding Standard	EN 10263-2-2001 Steel Rod,bars and Wire for Cold Heading and Cold Extrusion - Part 2: Technical Delivery Conditions for Steels Not Intended for Heat Treatment after Cold Working
Classification	Carbon Steel

C8C Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Al ^*
Minimum Value	0.06	-	0.25	-	-	0.02
Maximum Value	0.1	0.1	0.45	0.02	0.025	0.06

C8C Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %
5＜d≤100	+U or +U+PE	≤410	≥65
5＜d≤100	+AC or AC+PE	≤360	≥70
5＜d≤10	+U+C	≤490	≥63
10＜d≤40	+U+C	≥480	≥63
2＜d≤5	+U+C+AC	≤350	≥72
5＜d≤40	+U+C+AC	≤340	≥72
2＜d≤5	+U+C+AC+LC	≤390	≥68
5＜d≤40	+U+C+AC+LC	≤380	≥68
5＜d≤10	+AC+C	≤450	≥65
10＜d≤40	+AC+C	≤440	≥65

1 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN	Numerical Grade
ML08Al	U40088	SWRCH8A	1008	C8C	C8C	1.0213

2 Approximate Comparison Table High-Quality Carbon Structural Steel

3 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
YB	GB	JIS	ASTM	ISO	EN
QML08Al	ML08Al	SWRCH8A	1008	C8C	C8C

4 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China	Japan	International Organization for Standardization	European Standard
GB	JIS	ISO	EN	Numerical Grade
ML08Al	SWRCH8A	C8C	C8C	1.0213

5 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN
ML08Al	U40088	SWRCH8A	1008	CC8A	C8C

C8C Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!